ABSTRACT ASTM A provides three test methods to detect the presence of intermetallic precipitation in Duplex and Super Duplex Stainless Steels (DSS. manual Point Count) and ASTM A (Standard Test Methods for Detecting various tests which were carried out were ASTM A Test Method A, B and C . 30 Mar ASTM A provides three methods/practices to determine the extent of intermetallic precipitation in Duplex Stainless Steels. While Practice A.

Author: Kigal Mazura
Country: Peru
Language: English (Spanish)
Genre: Business
Published (Last): 25 August 2015
Pages: 278
PDF File Size: 14.8 Mb
ePub File Size: 18.73 Mb
ISBN: 191-9-96664-710-7
Downloads: 49552
Price: Free* [*Free Regsitration Required]
Uploader: Goltisar

The values given in astm a923 are for information only. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.

G2MT Laboratories

A number in parentheses indicates the year of last reapproval. The Charpy procedure as asgm applied is different from that as commonly applied for the determination of toughness and should not astm a923 used when characterization of material toughness is the purpose of the testing. Methods C through F are designed as incremental tests and require multiple specimens.

The speed of these precipitation reactions is a function of composition and thermal or thermomechanical history of each individual piece. Astm a923 us Contact us Aastm Terms of use. The pH is adjusted to 1. ASTM A was implemented to assess the presence of intermetallic phases in base material, but has also been used for weld qualification. Astm a923 of an international conference Oceanology: Asm material tested in a 6 wt.

Rapid cooling of the product provides the maximum resistance to astm a923 of detrimental phases by subsequent thermal exposures. The speed of these precipitation reactions is a function of composition and astm a923 or thermomechanical history of each individual piece.

The presence or absence of corrosion attack in this test is not astm a923 a a93 of the performance of the material in other corrosive environments; in particular, it does not provide a basis for predicting resistance to forms of corrosion not associated with the precipitation of intermetallic phases see Note 4.

X923 to Blog List. Because of the extensive testing required and time consuming nature, these tests are generally not astm a923 for production testing, even when acceptance criteria are provided.

Log in to your subscription

The presence of these phases is detrimental to toughness and corrosion resistance. This abstract is a brief summary of the referenced standard. Astm a923 energy for a subsize specimen is reduced in direct proportion to the reduced area of the subsize specimen relative to astm a923 of the full-size specimen. These test methods will not necessarily detect losses of toughness or corrosion resistance attributable to other causes.

A actually contains three different test methods for determining acceptability. When Astm a923 Method A is specified as an acceptance test, specimens having other than acceptable etch structures may, at the option of the producer, be ast by Test Method B or Test Method C. ASTM A includes three separate test methods that can be used to assess the extent of intermetallic precipitation, namely:.

Except for rapidly cooled material, it may be necessary to sample atm a location determined to be the most slowly cooled for the material piece to be characterized. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete astm a923 up to date.

B The acceptable minimum impact energy shall be agreed upon by seller and purchaser. Correct heat treatment of astm a923 stainless steel can eliminate these detrimental phases. Active view current version of standard.

astm a923 It is the responsibility of the user of this standard to establish astm a923 safety and health practices and determine the applicability of regulatory limitations prior to use. There are no acceptance criteria for any alloys. Proceedings of an international conference Diverless and Deepwater Techology: Publishers Content Coverage Privacy.

Because of the wide experience in the production testing of duplex alloys, testing in accordance with A is recommended. These tests identify the minimum critical temperature needed to initiate pitting or crevice corrosion. Peer reviewed only Published between: It is well known that the precipitation of intermetallics such as sigma phase and chi phase can promote loss of toughness, and loss astm a923 corrosion resistance.

Ferric Chloride Corrosion Testing – Rolled Alloys, Inc.

This test method may be used with other astm a923 tests to provide a rapid method for identifying those specimens that are free of detrimental intermetallic phases as measured in these other tests. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of astm a923 limitations prior to use. Sheriff’s Encyclopedic Dictionary of Applied Geophysics, fourth edition.

Nickel Alloy Seamless Tubes: It is the responsibility of the astm a923 of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Historical Version s – view previous versions of standard.